Technical conditions for plates of P265GH

1. Scope
The technical conditions apply to pressure vessel steel plates of P265GH with thickness not more than 250mm. (8mm-250mm).
2. Adopt standard:
EN10028-2: 2003 Flat products made of steels for pressure purposes Part 2: Non-alloy and alloy steels with specified elevated temperature properties
EN10163-2:2004 Delivery requirements for surface condition of hot-rolled steel plates, wide flats and sections - Part 2: Plate and wide flats Class B.
3. Dimension, Shape, Weight and Permissible Deviation
The dimension, shape, weight and permissible deviation shall meet the requirements of EN10029.
4. Technical conditions
4.1 Chemical composition (Ladle analysis)
The chemical composition of plates shall be accordance with the following table 1.
Table 1 Chemical composition (Ladle analysis)
C Si Mn P S Alt Cr Cu Mo Nb Ti V N
Max 0.20 Max 0.40 0.80- 1.40 Max 0.025 Max 0.015 Min 0.020 Max 0.30 Max 0.30 Max 0.08 Max 0.020 Max 0.030 Max 0.020 Max 0.012

4.2 Carbon equivalent (CEq)
Carbon equivalent shall be not more than 0.43 for plates of P265GH.
Carbon equivalent shall be calculated as follows:
CEq=C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15 (%)
4.3 Mechanical properties
The mechanical properties of P265GH shall meet the requirement as table 2.
Table 2 Tensile properties
Thickness mm Yield strength MPa Tensile strength MPa 0C Akv (J) Elongation %
8-60 Min 265 410-530 Min 34J Min 22
60-100 Min 245 410-530 Min 34J Min 22
100-150 Min 215 400-530 Min 34J Min 22
150-250 Min 200 390-530 Min 34J Min 22

4.4 SWHT: The optimized SWHT technology is as follows: heating at 610℃+/-10℃ for 7h, then followed by cooling in furnace to 400℃, then for air cooling.
4.5 Minimum values for the proof strength Rp0.2 at elevated temperatures shall meet the requirements per table 4.





Table 4 High temp Tensile properties
Test TEMP Thickness mm 300℃ 350℃ 400℃
Rp0.2
Min (MPa) 8-60 173 160 150
61-100 160 148 139
101-150 140 130 122
151-250 130 121 114

View More

Supporting Documents

No supporting documents found.

Business Details

Gloria Steel Limited
23-Oct-2013
China
Products for Sale (204)
Request for Quotations (0)
We're Gloria Steel from China and focusing on Iranian Oil and Gas fields services. Rely on our experienced processed tea...
Share in: